Lexan PC 500ECR Physical property
|
10 ％玻璃纖維填充,注射模壓級,非氯化非溴化阻燃UL - 94 V0(2.3mm),它有各種不透明的顏色. |
|
Property |
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL |
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 5 mm/min |
580 |
kgf/cm2 |
ASTM D 638 | |
|
Tensile Stress, brk, Type I, 5 mm/min |
480 |
kgf/cm2 |
ASTM D 638 | |
|
Tensile Strain, yld, Type I, 5 mm/min |
4.7 |
% |
ASTM D 638 | |
|
Tensile Strain, brk, Type I, 5 mm/min |
46 |
% |
ASTM D 638 | |
|
Tensile Modulus, 5 mm/min |
25000 |
kgf/cm2 |
ASTM D 638 | |
|
Flexural Stress, brk, 1.3 mm/min, 50 mm span |
950 |
kgf/cm2 |
ASTM D 790 | |
|
Flexural Modulus, 1.3 mm/min, 50 mm span |
31800 |
kgf/cm2 |
ASTM D 790 | |
|
Taber Abrasion, CS-17, 1 kg |
11 |
mg/1000cy |
SABIC Method | |
|
Tensile Stress, yield, 5 mm/min |
60 |
MPa |
ISO 527 | |
|
Tensile Stress, break, 5 mm/min |
45 |
MPa |
ISO 527 | |
|
Tensile Strain, yield, 5 mm/min |
5 |
% |
ISO 527 | |
|
Tensile Strain, break, 5 mm/min |
7 |
% |
ISO 527 | |
|
Tensile Modulus, 1 mm/min |
3300 |
MPa |
ISO 527 | |
|
Flexural Stress, yield, 2 mm/min |
95 |
MPa |
ISO 178 | |
|
Flexural Modulus, 2 mm/min |
3400 |
MPa |
ISO 178 | |
|
Hardness, H358/30 |
115 |
MPa |
ISO 2039-1 | |
|
IMPACT |
Value | Unit | Standard | |
|
Izod Impact, unnotched, 23°C, 6.4mm |
NB |
cm-kgf/cm |
ASTM D 4812 | |
|
Izod Impact, notched, 23°C |
13 |
cm-kgf/cm |
ASTM D 256 | |
|
Izod Impact, notched, -30°C |
10 |
cm-kgf/cm |
ASTM D 256 | |
|
Instrumented Impact Total Energy, 23°C |
622 |
cm-kgf |
ASTM D 3763 | |
|
Izod Impact, unnotched 80*10*3 +23°C |
NB |
kJ/m2 |
ISO 180/1U | |
|
Izod Impact, unnotched 80*10*3 -30°C |
130 |
kJ/m2 |
ISO 180/1U | |
|
Izod Impact, notched 80*10*3 +23°C |
10 |
kJ/m2 |
ISO 180/1A | |
|
Izod Impact, notched 80*10*3 -30°C |
8 |
kJ/m2 |
ISO 180/1A | |
|
Izod Impact, unnotched 80*10*4 +23°C |
NB |
kJ/m2 |
ISO 180/1U | |
|
Izod Impact, unnotched 80*10*4 -30°C |
NB |
kJ/m2 |
ISO 180/1U | |
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm |
10 |
kJ/m2 |
ISO 179/1eA | |
|
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm |
9 |
kJ/m2 |
ISO 179/1eA | |
|
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m2 |
ISO 179/1eU | |
|
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m2 |
ISO 179/1eU | |
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
9 |
kJ/m2 |
ISO 179/1eA | |
|
Charpy Impact, notched, 23°C |
15 |
kJ/m2 |
ISO 179/2C | |
|
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm |
NB |
kJ/m2 |
ISO 179/1eU | |
|
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm |
NB |
kJ/m2 |
ISO 179/1eU | |
|
THERMAL |
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50 |
154 |
°C |
ASTM D 1525 | |
|
HDT, 0.45 MPa, 3.2 mm, unannealed |
143 |
°C |
ASTM D 648 | |
|
HDT, 1.82 MPa, 3.2mm, unannealed |
136 |
°C |
ASTM D 648 | |
|
CTE, -40°C to 40°C, flow |
4.68E-05 |
1/°C |
ASTM E 831 | |
|
CTE, -40°C to 40°C, xflow |
8.46E-05 |
1/°C |
ASTM E 831 | |
|
Thermal Conductivity |
0.21 |
W/m-°C |
ISO 8302 | |
|
CTE, -40°C to 40°C, xflow |
8.46E-05 |
1/°C |
ISO 11359-2 | |
|
CTE, 23°C to 80°C, flow |
4.E-05 |
1/°C |
ISO 11359-2 | |
|
Ball Pressure Test, 125°C +/- 2°C |
PASSES |
- |
IEC 60695-10-2 | |
|
Vicat Softening Temp, Rate B/50 |
141 |
°C |
ISO 306 | |
|
Vicat Softening Temp, Rate B/120 |
143 |
°C |
ISO 306 | |
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm |
144 |
°C |
ISO 75/Be | |
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm |
136 |
°C |
ISO 75/Ae | |
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
136 |
°C |
ISO 75/Af | |
|
HDT/Ae, 1.8 MPa Annealed 120°C, 2hrs |
142 |
°C |
ISO 75/Ae | |
|
Relative Temp Index, Elec |
130 |
°C |
UL 746B | |
|
Relative Temp Index, Mech w/impact |
130 |
°C |
UL 746B | |
|
Relative Temp Index, Mech w/o impact |
130 |
°C |
UL 746B | |
|
PHYSICAL |
Value | Unit | Standard | |
|
Specific Gravity |
1.27 |
- |
ASTM D 792 | |
|
Mold Shrinkage, flow, 3.2 mm |
0.4 - 0.6 |
% |
SABIC Method | |
|
Mold Shrinkage, xflow, 3.2 mm |
0.4 - 0.6 |
% |
SABIC Method | |
|
Melt Flow Rate, 300°C/1.2 kgf |
7.5 |
g/10 min |
ASTM D 1238 | |
|
Density |
1.25 |
g/cm2 |
ISO 1183 | |
|
Water Absorption, (23°C/sat) |
0.31 |
% |
ISO 62 | |
|
Moisture Absorption (23°C / 50% RH) |
0.13 |
% |
ISO 62 | |
|
Melt Volume Rate, MVR at 300°C/1.2 kg |
7 |
cm210 min |
ISO 1133 | |
|
ELECTRICAL |
Value | Unit | Standard | |
|
Hot Wire Ignition {PLC) |
4 |
PLC Code |
UL 746A | |
|
High Ampere Arc Ign, surface {PLC} |
4 |
PLC Code |
UL 746A | |
|
Comparative Tracking Index (UL) {PLC} |
3 |
PLC Code |
UL 746A | |
|
Volume Resistivity |
>1.E+15 |
Ohm-cm |
IEC 60093 | |
|
Surface Resistivity, ROA |
>1.E+15 |
Ohm |
IEC 60093 | |
|
Dielectric Strength, in oil, 0.8 mm |
33 |
kV/mm |
IEC 60243-1 | |
|
Dielectric Strength, in oil, 1.6 mm |
25 |
kV/mm |
IEC 60243-1 | |
|
Dielectric Strength, in oil, 3.2 mm |
16 |
kV/mm |
IEC 60243-1 | |
|
Relative Permittivity, 50/60 Hz |
2.9 |
- |
IEC 60250 | |
|
Relative Permittivity, 1 MHz |
2.8 |
- |
IEC 60250 | |
|
Dissipation Factor, 50/60 Hz |
0.001 |
- |
IEC 60250 | |
|
Dissipation Factor, 1 MHz |
0.01 |
- |
IEC 60250 | |
|
Comparative Tracking Index |
150 |
V |
IEC 60112 | |
|
FLAME CHARACTERISTICS |
Value | Unit | Standard | |
|
UL Recognized, 94V-1 Flame Class Rating (3) |
1.8 |
mm |
UL 94 | |
|
UL Recognized, 94V-0 Flame Class Rating (3) |
2.3 |
mm |
UL 94 | |
|
Glow Wire Flammability Index 960°C, passes at |
1 |
mm |
IEC 60695-2-12 | |
|
Glow Wire Ignitability Temperature, 1.0 mm |
825 |
°C |
IEC 60695-2-13 | |
|
Oxygen Index (LOI) |
36 |
% |
ISO 4589 | |
|
UV-light, water exposure/immersion |
F2 |
- |
UL 746C | |
|
Processing |
| Parameter | ||
Injection Molding |
Value | Unit |
|
Drying Temperature |
120 |
°C |
|
Drying Time |
2 - 4 |
hrs |
|
Maximum Moisture Content |
0.02 |
% |
|
Melt Temperature |
290 - 320 |
°C |
|
Nozzle Temperature |
280 - 310 |
°C |
|
Front - Zone 3 Temperature |
290 - 320 |
°C |
|
Middle - Zone 2 Temperature |
280 - 310 |
°C |
|
Rear - Zone 1 Temperature |
270 - 300 |
°C |
|
Hopper Temperature |
60 - 80 |
°C |
|
Mold Temperature |
80 - 120 |
°C |
- Physical properties of related products: 503R 500R SP7602 3412R SP7604 3414R 3413R BFL2010 BFL2015 3412ECR 500 503 LF1520A
Correlation search: 500ECR-131 500ECR-739 500ECR-BK1066 500ECR-NA Lexan 500ECR 500ECR物性 Sabic 500ECR GE 500ECR PC 500ECR 聚碳酸酯 PC 塑膠原料 Sabic PC PC 塑料
廣州華秀塑膠有限公司不僅是專業的Lexan PC 500ECR原料供應商，亦注重技術支持及全方位的解決方案，提供從材料鑒定、模具設計、成型加工等系列幫助，亦可為客戶量身定制各特殊性能之Lexan PC 500ECR材料，進而協助客戶提高產品竟爭力。
地址:廣州市天河區中山大道中439號東圃天銀商貿大廈1720-1723室
電話:020-82582555
傳真:020-82523699
Email: sales@va-so.cn
Lexan PC 500ECR報價 >>
常規產品
長纖增強尼龍66 長纖增強PPA
長纖增強尼龍6 長纖增強PP
長纖增強復合材料 沖擊改性復合尼龍66
沖擊改性復合尼龍6 高強尼龍
沖擊改性復合尼龍 沖擊改性復合材料
改性PP 改性的合金料
高溫改性塑料 含氟聚合物
改性POM 改性PBT
改性PC 焊接用復合塑料
高比重復合塑料 永久防靜電塑料
永久防靜電ABS 永久防靜電合金
永久防靜電POM 其他導電材料
導電尼龍 導電PE,導電PP
高溫導電塑料 導電POM
導電PBT 導電PC
其他非PTFE自潤滑塑料 非PTFE自潤滑PA
非PTFE自潤滑聚苯醚 非PTFE自潤滑PPA
非PTFE自潤滑聚甲醛 非PTFE自潤滑聚碳酸酯
其他潤滑塑料 潤滑尼龍
潤滑烯烴 潤滑PPO(PPE+PS)
耐熱潤滑塑料 潤滑POM
潤滑PBT 潤滑彈性體
潤滑PC 擠出PBT
熱傳導復合塑料 其他PC
EMI/RFI屏蔽復合塑料 預著色非填充樹脂
長纖增強尼龍6 長纖增強PP
長纖增強復合材料 沖擊改性復合尼龍66
沖擊改性復合尼龍6 高強尼龍
沖擊改性復合尼龍 沖擊改性復合材料
改性PP 改性的合金料
高溫改性塑料 含氟聚合物
改性POM 改性PBT
改性PC 焊接用復合塑料
高比重復合塑料 永久防靜電塑料
永久防靜電ABS 永久防靜電合金
永久防靜電POM 其他導電材料
導電尼龍 導電PE,導電PP
高溫導電塑料 導電POM
導電PBT 導電PC
其他非PTFE自潤滑塑料 非PTFE自潤滑PA
非PTFE自潤滑聚苯醚 非PTFE自潤滑PPA
非PTFE自潤滑聚甲醛 非PTFE自潤滑聚碳酸酯
其他潤滑塑料 潤滑尼龍
潤滑烯烴 潤滑PPO(PPE+PS)
耐熱潤滑塑料 潤滑POM
潤滑PBT 潤滑彈性體
潤滑PC 擠出PBT
熱傳導復合塑料 其他PC
EMI/RFI屏蔽復合塑料 預著色非填充樹脂
熱門工程塑膠原料
RVL28 RCL36 RE0029 DE0029 RL0049S ML6622R EFP36G DEP42E 420U KF002 RFL32 K3000 BDT5510 RD000I LS1 NORYL™ PPO LEXAN™ PC VALOX™ PBT ULTEM™ PEI CYCOLOY™ PC/ABS XYLEX™ PC/PET XENOY™ PC/PBT/PET Noryl GTX PPE/PA CYCOLAC™ ABS GELOY™ ASA Colorcomp Faradex Konduit Lubricomp Lubriloy Stat-kon Stat-loy Thermocomp Thermotuf Verton